resin content

Increasing the temperature of preheating, the mandrel-pressure roller and the hot air gun and choosing the moderate pressure of pressure roller come along with a rise in interlaminar shear strength ( ILSS) and a reduction in resin content.

结果表明：提高芯模压力辊温度、热风枪温度、预热器温度，选择适中的压力辊压力，在层间剪切强度提高的同时，树脂含量下降。

互联网摘选

Experimental results show that with crisscross winding method and 30% to 40% of resin content and 150 N to 200 N of winding tension for a fiber strand and GPC chart analysis to determine curing time, better comprehensive performance of the composite materials can be obtained.

结果表明：采用交替铺层方式缠绕成型，含胶量控制在30%～40%（质量分数），缠绕张力控制在150N～200N，采用GPC谱图控制固化时机，得到的复合材料综合性能较好；

互联网摘选

Adding 4.0% YZ-1 could make the content of free formaldehyde reduce to 0.22% when the initial content of free formaldehyde in the resin was 2.00%-6.00%.

当初始游离甲醛含量在2.00%-6.00%时，YZ-1的施加量为4.0%，可使游离甲醛含量降至0.22%。

互联网摘选

Research of Analysis Method for Fluorocarbon Resin Content in Fluorocarbon Lacquer

氟碳漆中氟碳树脂含量的分析方法研究

互联网摘选

The monomer ratio, CPE content, swelling time, conversion and the amount of mercaptan would also affect the light-trasmitting property of MCS resin.

单体配比、CPE用量、溶胀时间、转化率及硫醇用量等均有影响。

互联网摘选

Under different test temperature, modification effect of Epoxy resin and its content was judged upon viscous-elastic characters of asphalt mixtures.

在不同的试验温度下，考察了环氧树脂及其用量对沥青混合料粘弹特性的影响效果。

互联网摘选

The Resin Content on-line Monitoring in Composite Prepreg Tapes Using Beta-ray Technique

用β射线技术在线监测复合材料预浸带树脂含量

互联网摘选

The article describes the control of resin content and GRP product quality.

本文叙述了手糊玻璃钢制品的含胶量控制与质量的关系.

互联网摘选

The influence of the resin content on temperature and pressure in the hot-pressing process of flakeboard is illustrated for first time based on the experiment results: ( 1) consuming adhesive is favorable to the heat transfer process on the direction of thickness.

首次通过实验阐明了施胶量对刨花板热压过程中温度和压力的影响：（1）施加胶粘剂有利于板坯厚度方向上的传热。

互联网摘选

The crystallinity reach its peak when the content of epoxy is 1%, with the increase of epoxy resin content, the crystallinity of nylon 11 alloy decreases.

环氧树脂用量为1%时，尼龙11共混合金体系的结晶度最大，此后随着环氧树脂的加入，尼龙11结晶度随之降低。

互联网摘选

When resin content was 4%, the wheat-straw particleboard of 0. 6g/ cm3 could fully meet requirement;

当施胶量为4%时，密度为0.6g／cm3的麦秸刨花板的力学性能完全满足国家标准要求；

互联网摘选

The bonding strength between Portland cement with wood was affected with cold pressing, curing age and resin content.

木材与水泥的结合强度受胶合压力、养护时间、施胶量以及胶合纹理的影响。

互联网摘选

Books and periodicals on the cohesion and effectiveness of resin content, gummed coating thickness and grooving.

书刊的黏结效果与上胶量 、 背胶的涂布厚度及开槽大小有关.

网络文摘精选

Calculation of Bleeding System in Composite Autoclave Forming and Selection of Prepreg Resin Content

热压罐法复合材料成形吸胶系统的计算及预浸料树脂含量的选择

互联网摘选

Using the blend of epoxy resin and phenolic resin as binder, whose functional group molar ratio was 1:3, and the total resin content was 17wt%.

粘结剂使用EP和PF的共混树脂，其官能团摩尔比为1：3，总树脂含量为17wt%。

互联网摘选

The Influence of Resin Content on the Thermal Properties of Shell Mold Sand

树脂添加量对壳型覆膜砂热性能的影响

互联网摘选

However, to the acacia flakeboard with the same density, whether the resin content is high or not, the pressure of the central layer of mat is fluctuating, but always keeps it in the horizontal direction, the 3 pressing phase is not emerged.

同样密度的刺槐刨花板，不论施胶量大小，板坯芯层压力波动大，但几乎保持水平方向，没有出现三段压力之分。

互联网摘选

But the thermal resistance of resin enhanced when urea content was increased.

但随着脲基含量的增加，树脂的耐热性提高。

互联网摘选

Continuous monitoring of resin content in carbon/ phenolic prepreg cloth by β-ray method

炭/酚醛预浸布树脂含量的β-射线连续监测

互联网摘选

Study on the optimal resin content of high strength bulletproof glass fiber reinforced plastics

防弹用纤维复合材料最佳树脂含量研究

互联网摘选

The low viscosity and good flexibility epoxy acrylate with different molecular weight and content was successfully prepared by firstly making modification of epoxy resin with maleic anhydride and polyethylene glycol monoester, and then modified epoxy resin react with acrylic acid.

采用马来酸聚乙二醇单酯对环氧树脂进行改性，然后用丙烯酸酯化，制得光固化涂料用一系列低黏度、柔韧性好的环氧丙烯酸酯。

互联网摘选

Single face corrugated machine speed slow increases Corrugating cord to peak cohniiand resin content.

单面瓦楞机车速过慢,会增大瓦楞楞峰的着胶量.

互联网摘选

Glued resin content affected longitudinal tensile strength significantly and the impacting of board density to all mechanical properties reached to a significant level. In the testing range other factors and levels affected the board properties indistinctively.

单板涂胶量对板材顺纹抗拉强度影响达到显著水平，板材密度对各力学性能影响均达到显著水平；其余因素各水平在试验选定范围内，并未对板材各性能指标有显著的影响。

互联网摘选

The resin content put little influence on the temperature changes in central layer of the acacia flakeboard.

施胶量对刺槐刨花板芯层温度影响非常小。

互联网摘选