The results show that the resistance of mortar to thaumasite form of sulfate attack ( TSA) increases with the reduction of water-cement ratio.

1、

Results show that paste containing ground limestone can be destroyed at the temperature of 0& 10 ℃ by the sulphate attack of thaumasite form.

结果表明：掺石灰石粉的水泥石在0~10℃的温度范围内，可形成碳硫硅钙石的硫酸盐侵蚀破坏。

互联网摘选

2、

Dry-wet circulation and carbonation influencing on the concrete sulfate attack Thaumasite form of sulfate attack of cementitious materials

干湿交替和碳化对混凝土硫酸盐侵蚀的影响水泥基材料碳硫硅钙石型硫酸盐腐蚀

互联网摘选

3、

This is the first discovery of thaumasite form of sulfate attack in China. Thaumasite form of sulfate attack on concrete

这是在我国发现的首例碳硫硅钙石型硫酸盐腐蚀。混凝土中Thaumasite硫酸盐侵蚀的形成与特征

互联网摘选

4、

The sulphuric acid has eaten into these steel pipes. Thaumasite form of sulfate attack of cementitious materials

硫酸已腐蚀了这些钢管。水泥基材料碳硫硅钙石型硫酸盐腐蚀

互联网摘选

5、

Effects of temperatures on thaumasite formation

温度对碳硫硅钙石形成的影响

互联网摘选

6、

Thaumasite form of sulfate attack on concrete

混凝土中Thaumasite硫酸盐侵蚀的形成与特征

互联网摘选

7、

Last by admixture added explore inhibiting Thaumasite sulfate attack in cementitious systems.

通过在胶凝材料体系加入外加剂探索抑制Thaumasite型硫酸盐侵蚀的方法。

互联网摘选

8、

Thaumasite is prone to decomposed easily in the high concentration of CO2.

碳硫硅钙石在高浓度CO2作用下容易发生分解。

互联网摘选

9、

Becoming architecture Structural characteristic, forming mechanism and the conditions conducive to formation of thaumasite are discussed.

分析了Thaumasite的物相结构特征、生成条件和破坏机理；

互联网摘选

10、

The formation reaction affect different admixtures Thaumasite.

研究了不同外加剂对Thaumasite形成反应影响。

互联网摘选

11、

Thaumasite Formation and Effect on Limestone Cement Concrete

碳硫硅钙石的形成及其对混凝土性能的影响

互联网摘选

12、

Test methods for thaumasite form of sulfate attack

碳硫硅酸钙型硫酸盐侵蚀测试方法

互联网摘选

13、

Thaumasite form of sulfate attack in the concrete of Yong'an dam

新疆永安坝混凝土的碳硫硅钙石型硫酸盐腐蚀

互联网摘选

14、

Thaumasite form of sulfate attack on different variety of cement

不同品种水泥的抗碳硫硅酸钙型硫酸盐侵蚀性能

互联网摘选

15、

Research on Influence Factor of the Thaumasite Form of Sulfate Attack on Cement Concrete

水泥混凝土TSA侵蚀影响因素研究

互联网摘选

16、

A summary of the research on thaumasite form of sulfate attack

碳硫硅钙石型硫酸盐腐蚀研究综述

互联网摘选

17、

Research on Influencing Factors of Thaumasite Form of Sulfate Attack Towards Cement Based Materials

水泥基材料碳硫硅钙石型硫酸盐侵蚀影响因素研究

互联网摘选

18、

Structural Characteristic and Formation Mechanism of Thaumasite and Its Destruction Effect on Concrete

Thaumasite的结构、形成机理及对混凝土的破坏作用

互联网摘选

19、

This form of attack directly leads to the decomposition of CSH gel and formation of the non-binder thaumasite crystal in the cement paste. As a result, the attacked concrete becomes a white mushy and friable mixture.

它直接导致水泥石中CSH凝胶体的分解，生成无任何胶结性的硅灰石膏（thaumasite）晶体，使混凝土最终变为一种白色的烂泥状混合物。

互联网摘选

20、

Discovery of thaumasite in China

我国发现的硅灰石膏水泥基材料中的碳硫硅钙石

互联网摘选