Although lower tensile strength and tear strength, color fastness of deacetate fabric were better than that of viscose fabrics.

The physical indices such as tensile strength, elongation and tear strength before and after the dye-fixation were tested.

并且对固色前后断裂强力、伸长、撕破强力等物理指标进行了测试。

互联网摘选

The experiment results showed that the tear strength, the modulus at 20% and the swelling resistance increased as the length of the fibre increased;

实验结果表明：这两种短纤维橡胶复合材料的撕裂强度、20%定伸应力随短纤维长度增加而增大，抗溶胀能力增强；

互联网摘选

Tear strength and tensile strength of PE film will decline with increasing of content of filling, but moisture coefficient and gas permeability will increase.

随着填料含量的增加，聚乙烯薄膜的撕裂强度和拉伸强度随之下降。而透湿系数和透气性能随之增加。

互联网摘选

Tensile stress-strain tests and tear strength were test by AIPU ALJ-02 tensile testing machine. 4.

使用AIPU ALJ-02型双数显拉力试验机对其进行拉伸应力应变测试、撕裂强度测试。

互联网摘选

Results: The tear strength of SY-1 silicon rubber was better than that of MDX4-4210 silicon rubber.

结果：SY-1硅橡胶吸水率、溶解率性能差于MDX4-4210硅橡胶，撕裂强度优于MDX4-4210硅橡胶。

互联网摘选

The film made of metallocene polyethylene resin possessed good transparence and exhibited superior dart impact strength and tear strength.

用所得茂金属聚乙烯树脂加工成的薄膜具有较好的透明性，并表现出了优异的落镖冲击强度和撕裂强度。

互联网摘选

Rubber and plastics-Analysis of multi-peak traces obtained in determinations of tear strength and adhesion strength

GB/T12833-1991橡胶和塑料撕裂强度及粘合强度多峰曲线的分析方法

互联网摘选

The coupling agent A-172 had a more significant modifying effect and gave EPDM vulcanizate much higher tear strength;

偶联剂A-172的改性作用较为明显，可显著提高EPDM硫化胶的撕裂强度；

互联网摘选

" Rubber, vulcanized-Determination of tear strength of small test pieces ( Delft test pieces)"

GB/T12829-1991硫化橡胶小试样（德尔夫特试样）撕裂强度的测定

互联网摘选

The cause leading to deviation of tear strength in measuring tear strength of silicone rubber vulcanizate was analyzed.

分析了在热硫化硅橡胶混炼胶撕裂强度的测试中撕裂强度出现偏差的原因；

互联网摘选

The results showed that the tensile strength, elongation at break and tear strength increased with the OMMT content increasing.

测试结果表明，随着蒙脱土用量的增加，复合材料的定伸应力、拉伸强度和撕裂强度均大幅度提高。

互联网摘选

Tear strength of the blend was improved obviously and kept the characteristic of great elongation as elastomer simultaneously.

尼龙树脂原位生成的短纤维可明显提高共混硫化胶的撕裂强度，同时使其保持了弹性体高伸长率的特性。

互联网摘选

When nanocomposites were prepared by solution method, the tensile strength and tear strength increased, but dielectric loss decreased.

采用溶液混炼法制备复合材料时，SR的拉伸强度、撕裂强度明显提高，介电损耗降低。

互联网摘选

Study on tear strength of the abraded denim

牛仔布摩擦后撕破强力的研究

互联网摘选

The wood obtained had heavier wood basic volume weight and higher tensile, burst and tear strength of paper.

浆纸物理强度：裂断长，耐破与撕裂两项综合强度指数均大于对照。

互联网摘选

For instance, 300% modulus was increased by 77% and tear strength by 38%.

例如，300%定伸应力提高了77%，抗撕裂强度提高了38%。

互联网摘选

The best tear strength was found in the paper sheets made from pulp of root-wood.

根材的撕裂强度最好。

互联网摘选

Tensile strength and tear strength of composites reach the maximum when fiber content is 6%.

纤维含量为6%时，复合材料的拉伸强度和撕裂强度最大。

互联网摘选

Consider the bursting strength that is required and the tear strength desired.

考虑爆破强度是必需的，所需的撕裂强度。

互联网摘选

At a certain cutting angle, smaller cutting angle results in stronger tear strength;

割口角度一定时，割口深度小的试样的撕裂强度反而大；

互联网摘选