barium glass

Conclusions: The absorption behavior of a silane coupling agent γ-MPS was revealed on the barium glass surface, which provided the theoretical basis for the development of dental composite resins.

结论：揭示了硅烷偶联剂γ-MPS在钡玻璃表面的吸附特征，为新型复合树脂的研究和开发提供理论依据。

互联网摘选

Study of adsorption mechanism of the silane coupling agent onto the surface of barium glass

硅烷偶联剂γ-MPS在钡玻璃表面吸附机制的研究

互联网摘选

Results: When the concentration of γ-MPS was low, the γ-MPS molecules oriented either parallel or perpendicularly onto the barium glass surface.

结果：γ-MPS低浓度时，分子在钡玻璃表面的吸附既有垂直取向又有平行取向；

互联网摘选

Effect of concentration of silane coupling agent on bonding strength of barium glass to resin matrix

硅烷偶联剂的浓度对钡玻璃与树脂基质间粘接强度的影响

互联网摘选

Results The relationship tallied with negative linear correlation between the K-M function values of the isolated OH-groups on the barium glass surface and the concentrations of γ-MPS.

结果钡玻璃表面游离羟基的K-M函数值与γ-MPS质量分数存在负相关的直线相关关系。

互联网摘选

When the content of 3wt% silane-treated barium glass filler reached 40wt%, simultaneously added 3wt% nano-sized silic into resin matrix, the experimental composite obtained optimal mechanical properties and suitable viscosity. 5.

当3wt%硅烷偶联剂处理后的钡玻璃填料在树脂体系中含量达到40wt%，同时加入3wt%的二氧化硅纳米填料，可以获得较佳的复合树脂力学性能和适合的树脂体系粘度。

互联网摘选

Based on the research in the medium and strong polar glass capillary column, the coating on the barium sulfate micro crystal modified surface with apolar and weak polar liquid phase is investigated.

本文在中等极性和强极性玻璃毛细管柱研究的基础上，对弱极性和非极性固定液在硫酸钡微晶改性表面上的涂渍情况作了详细的研究。

互联网摘选

Each γ-MPS molecule occupied 0.21 nm~ 2 when the monomolecular coverage was formed on the barium glass surface.

γ-MPS在钡玻璃表面单分子层覆盖所占据的面积为每分子0·21nm2。

互联网摘选