Experimental results indicate that the surface wear profile of micro-arc oxidized ceramic layers is regular and the hardness of ceramic layers is 10 times more than that of substrate.

实验结果表明，微弧氧化陶瓷膜层的表面磨损外观比较均匀，磨损痕迹也比较轻微，其表面硬度达到2500HV，是基体的10倍以上。

互联网摘选

The surface hardness of the micro-arc oxidation layers can be measured by use of the 71-optics micro sclerometer, after the Gold sputtering treated;

借助表面喷金前处理，使用显微硬度仪测量出了微弧氧化陶瓷层表面硬度。

互联网摘选

It was pointed out that there still exist some disadvantages in the related theoretical research and production cost control of the micro-arc oxidation technology, though it has a promising application perspective.

同时指出微弧氧化技术虽具有广泛的应用前景，但在理论研究和生产成本控制等方面仍存在不足之处。

互联网摘选

Research on Corrosion Resistance of Magnesium Alloy with Micro-arc Oxidation Film Stuffed up with Organic Coating

镁合金微弧氧化膜有机封孔耐腐蚀性能的研究

互联网摘选

TEM Analysis of the micro-arc Oxidation Coatings on Magnesium alloys in a Aluminate Alkalinous electrolytic solution

铝酸盐电解液中镁合金微弧氧化TEM分析

互联网摘选

Ceramic coatings containing Ca and P have been successfully formed on the surface of Mg alloys by Micro-arc oxidation ( MAO) in this paper.

本文采用微弧氧化处理的方法成功地在AZ31Mg合金表面制备了含Ca、P的陶瓷层。

互联网摘选

Effect of Cathode Current Density on Coating of ZrO_2 Prepared by Micro-arc Oxidation

阴极电流密度对微弧氧化ZrO2陶瓷膜及耐蚀性的影响

互联网摘选

On effect of silver deposition on photocatalytic activity of TiO_2/ Ti using micro-arc oxidation

Ag沉积对微弧氧化TiO2/Ti膜光催化性能的影响

互联网摘选

It could be observed that the SiO_2 sol sealing agent fills up the hole of micro-arc oxidation coating on magnesium alloy.

SiO2溶胶封孔剂可浸入镁合金微弧氧化膜的微孔，形成有效封孔。

互联网摘选

The studies of load on the micro-arc oxidation have found that it is highly capacitive, equivalent to the RC topology.

而对微弧氧化负载的研究发现，它具有很强的容性，可用RC拓扑结构来等效。

互联网摘选

The effect of micro-arc discharge of the Ti anode on the decolorization of methyl orange was studied.

以Ti为阳极研究了微弧放电对污水的处理效果，发现放电条件下对甲基橙的脱色效果显著。

互联网摘选

Effect of Electrical Parameters on Preparing TiO_2 Bioceramic Coatings on Titanium Alloy by Micro-arc Oxidation Technique

电参数对钛合金微弧氧化法制备TiO2生物陶瓷涂层的影响

互联网摘选

Microstructure characterization of micro-arc oxidation treated SiC_p/ ZL109 aluminum matrix composites

SiC p/ZL109铝基复合材料微弧氧化层的微观组织特征

互联网摘选

The Effect of SiO_3~ ( 2-) on Micro-Arc Oxidization Ceramic Layer of TiAl Alloy

SiO3~（2-）对TiAl合金微弧氧化陶瓷层的影响

互联网摘选

Direct synthesis of CaTi_4 ( PO_4)_6 bio-ceramic film by micro-arc oxidation

微弧氧化法直接合成CaTi4（PO4）6生物陶瓷膜

互联网摘选

The Influence of Neodymium on Thickness and Surface Quality of Micro-arc Oxidation Ceramic Coating

Nd对镁合金微弧氧化陶瓷层厚度及表观质量的影响

互联网摘选

Effect of Additives on Wear Resistance of Micro-arc Oxidation Coating on TiAl Alloy

添加剂对TiAl合金微弧氧化膜耐磨性的影响

互联网摘选

Deposition of Stainless Steel 316L onto Steam Turbine Blades by High-energy Micro-arc Process

汽轮机叶片钢高能微弧沉积316L不锈钢涂层的试验研究

互联网摘选

Effect of Na_2WO_4 on properties of micro-arc oxidation ceramic coatings on aluminum alloy

Na2WO4对铝合金表面微弧氧化陶瓷层性能的影响

互联网摘选

The results show that in the initial stage of micro-arc oxidation the obtained ceramic coating is compact and nearly no microflaw can be observed, the microflaws like holes begin to appear in the exterior and finally irregular holes fill with 90% of the thickness range.

结果表明：微弧氧化初期，陶瓷层致密，几乎观察不到显微缺陷，随着处理时间的延长及陶瓷层的增厚，其外侧开始出现孔洞类缺陷，直至90%厚度范围布满相互交错的不规则孔洞；

互联网摘选